3003-H14:

BACK TO SPECIALTY PRODUCTS PAGE

Disclaimer: The content of this page is for general information only and is not to be used for engineering or design. The content of this material specification page was compiled from available public sources and authorities on material properties. Although we believe the information to be correct, Metal Stock, Inc. is not responsible for the accuracy of any of the material specifications and only presents this data as general information for our customers.

3003-H14 aluminum is alloyed with 1.20% manganese, which increases the strength of 3003 over commercially pure aluminum (1100 series). 3003 has excellent workability, weldability, and good corrosion resistance. It is used for drawing, forming, spinning, fuel tanks, sheet metal works, and other applications that require moderate strength for an aluminum with good weldability. H14 designates the temper and means that 3003 has been strain hardened and partially annealed. In this condition, 3003 can be easily formed. Embossing or debossing 3003 in this temper should not strain or crack the aluminum.

3003-H14 conforms to ASTM BB209, QQ-A-250/2, AMS 4006, AMS 4008.

 

General Information about 3003-H14:


APPLICATIONS:

3003-H14 is widely used for stampings, spun and drawn parts and products, cooking utensils, chemical equipment, builders hardware, storage tanks, truck and trailer components, mailboxes, cabinets, fan blades, awnings, siding, kitchen equipment, decorative trim, architectural uses, or signage applications. Where greater strength is required, consider 5052-H32.

MACHINING AND WELDING:

3003-H14 has a machinability rating of 97% when compared to 2011 at 100%.

3003-H14 can be readily welded using all the common welding techniques.


HEAT TREATING - Forging, Normalizing, and Annealing:

3003-H14 is not heat treatable.

 

 

BACK TO SPECIALTY PRODUCTS PAGE